Method for producing a composite electrode for electrochemical components, and a composite electrode

ABSTRACT

The invention concerns a method to produce a layer electrode for electrochemical components with a layer ( 2, 14 ) applied to a metal film ( 3 ), whereby to produce a connection between the metal film ( 3 ) and the layer ( 2, 14 ) a surface section ( 1 ) of the layer ( 2 ) is pressed over a part of the thickness (D) of the layer ( 2 ) into the softened metal film ( 3 ), and whereby the metal film ( 3 ) is softened during the pressing. Furthermore, the invention concerns the layer electrode. The ohmic resistance of the layer electrode can be reduced in an advantageous manner via the pressing of surface sections  1 ) of the layer ( 2, 14 ) into the metal film ( 3 ).

[0001] The invention concerns a method to produce a layer electrode for electrochemical components, whereby a layer is connected with a metal. Furthermore, the invention concerns a layer electrode for electrochemical components.

[0002] From the printed publication EP 0 786 142, electrochemical components are known in the form of electrochemical double-layer capacitors in which carbon layers are used as layer electrodes. In order to be able to contact the carbon of the carbon fabric with an aluminum electrode, the carbon fabric is first coated with liquid aluminum by means of an arc method. It is thereby achieved that the aluminum penetrates as deep as possible in the fibers of the carbon fabric, whereby a good electrical contact can be produced.

[0003] However, this method has the disadvantage that the hot aluminum easily oxidizes in the air and, due to the aluminum oxide layer thereby ensuing, the electrical contact resistance between the layer and the aluminum metal is increased.

[0004] Furthermore, the known method to produce a layer electrode has the disadvantage that the arc method requires a high mechanical stability of the layer in order to prevent a tear of the layer. In order to achieve the lowest ohmic resistance between carbon material and the material discharging or, respectively, supplying current in an electrochemical double-layer capacitor, a large-surface direct contact must be generated between the carbon material and the metal.

[0005] A high mechanical stability of the layer means that the layer must be implemented with a relatively large thickness, whereby the area available for the contact with a metal electrode is reduced, which results in an increase of the ohmic resistance of the capacitor. Moreover, stable carbon layers require the use of expensive, stable fiber materials, which means increased raw material costs.

[0006] In the further course of the production, a coated layer is positioned on the top or, respectively, underside of an aluminum film. This aluminum film serves as a discharge electrode for the capacitor. This arrangement from a plurality of parts (film and layers) must be manipulated without shifting in the assembly of a capacitor winding, in order to prevent short circuits on the edge of the film as well as a damage of the carbon layers.

[0007] Furthermore, the known method has the disadvantage that it requires a plurality of individual work steps. The aluminum introduced into the layer via the arc method increases the layer thickness of the layer, whereby the volume utilization of the of the capacitor is worsened.

[0008] It is therefore the object of the present invention to specify a method to produce a layer electrode, whereby layers with lower mechanical stability can be manipulated, and that is simple to implement.

[0009] This object is achieved by the inventive method according to patent claim 1. Further developments of the invention and a layer electrode produced with the inventive method are to be learned from the further patent claims.

[0010] The invention specifies a method to produce a layer electrode for electrochemical components with a layer applied to a metal film, whereby to produce a connection between the metal film and the layer a surface section of the layer is pressed into the metal film over a part of the thickness of the layer, and whereby the metal film is softened during the pressing.

[0011] The inventive method abandons the application of liquid aluminum to the layer in the arc method, whereby the mechanical stress for the layer is reduced. Layers with lower mechanical stability, and thus either layers with smaller layer thicknesses or layers produced from cheaper raw materials can thereby be used.

[0012] The use of thinner layers has the advantage that a total quantity of layer material (for example, carbon) to be placed in layers in the component can be distributed to a greater number of electrode layers, whereby the area available for the contacting of the layer with an electrode is increased. The ohmic resistance of the component to be realized thereby decreases, and therewith its losses, in an advantageous manner.

[0013] The danger of the oxidation of the metal is also reduced via the abandonment of the arc method, whereby the ohmic resistance of the layer electrode can be reduced.

[0014] Since sprayed-on aluminum is abandoned, the layer thickness of the layer electrode can be reduced, whereby the volume utilization increases in the component to be realized.

[0015] However, the layer thickness saved via the abandonment of the sprayed-on aluminum or, respectively, via the use of thinner layers can also be balanced by use of thicker aluminum films, whereby in the end effect the layer thickness of the layer electrode remains the same. However, the ohmic resistance of the layer electrode or, respectively, of the component to be realized is reduced, since thicker aluminum films enable a lower-ohmic connection to an external connection of the component.

[0016] Furthermore, the inventive method has the advantage that it comprises very few process steps, and thereby is cost-effective and simple to realize.

[0017] Moreover, the pressing of the layer into the softened metal film provides for an optimal electrical contact between layer and metal film.

[0018] In an advantageous embodiment of the invention, a layer comprising elementary carbon can be used as a layer, such as it is necessary, for example, for the realization of electrochemical double-layer capacitors.

[0019] Moreover, an aluminum film can be used as a metal film, as it is typical in the assembly of electrochemical double-layer capacitors.

[0020] The invention can be realized in that a layer stack with a layer lying over a metal film lies between a pressing tool and a stop, and whereby the layer stack is pressed by the pressing tool against the stop.

[0021] Moreover, a method is advantageous wherein a layer stack with a layer lying over a metal film lies between a pressing tool and a stop, and whereby the pressing tool presses the layer stack against the stop.

[0022] In an embodiment of the invention, the pressing tool can be provided with a flat surface that is pressed against the likewise flat surface of the stop. The pressed surface section of the layer can thereby be produced coherently, whereby the layer is pressed into the metal foil over its entire surface. In particular a deep connection of the metal foil with the layer, and correspondingly a lower ohmic resistance of the layer electrode, can thereby be effected. The flat surface can thereby be level or curved.

[0023] In the realization of an electrochemical double-layer capacitor, only the portion of the carbon layer that is not coated by metal contributes to the capacity. Correspondingly, it can be advantageous to press the layer into the metal film only in sections. The sections of the layer lying free on the metal film can thus contribute fully to the capacity of the component. Such a layer electrode can be produced in that a surface of the pressing tool exhibiting depressions is pressed against a stop whose surface is fashioned such that the layer is not pressed into the metal film at the locations of the depressions.

[0024] Furthermore, it is particularly advantageous when the metal film is softened in the proximity of the pressing tool or, respectively, the surface section to be pressed in. It can thereby be achieved that the thermal stress and also the mechanical stress of the aluminum film is kept as small as possible, which enables the use of thinner aluminum films. The volume utilization of a capacitor can thereby be improved.

[0025] The softening of the metal film can, for example, be achieved via a heated pressing tool and/or stop.

[0026] A further possibility to soften the metal film is to run an electrical current through the film, perpendicular to the film. Such an electrical current could, for example, be caused via application of corresponding electrical potentials at pressing tool and stop. In this case, pressing tool and stop must be electrically conductive.

[0027] Furthermore, it is also possible to effect the softening of the foil via emission of ultrasound. For this purpose, it is advantageous to use a pressing tool or, respectively, a stop that can emit ultrasound.

[0028] In order to achieve a still deeper connection of the layer with a metal, before the pressing of the layer into the metal film a metal powder can be applied to the surface section to be pressed in. Due to its smaller structural size, the metal powder is particularly easily permeate in the layer [sic], and thus a good electrical contact is produce [sic] between the metal film and the layer.

[0029] Furthermore, it is advantageous when a metal film are [sic] covered on both sides with two congruent layers, and these layers are connected with the metal film with the inventive method.

[0030] A metal film can thereby be effective as a discharge electrode for two layers, whereby the layer thickness of the layer electrode is optimally used.

[0031] In a further advantageous embodiment of the invention, a cylindrical roller rotating around a cylinder axis can be used as a pressing tool that rolls on the layer stack, with which surface sections of the layer are continuously pressed into the metal film.

[0032] In a further exemplary embodiment of the invention, the layer stack exhibits the shape of a ribbon, a stamp that can be moved transverse to the layer is used as a pressing tool. The following steps are implemented:

[0033] a) pressing of the stamp and the intermediate length section of the ribbon against a stop

[0034] b) movement of the stamp to release to ribbon

[0035] c) movement of the ribbon in the lengthwise direction by means of a ribbon transport device.

[0036] A discontinuous method is thereby available that in particular is suitable for the production of layer electrodes in sections.

[0037] In order to largely prevent an oxidation of the metal film, in an advantageous embodiment of the invention the production of the connection between the layer and the metal film can ensue in a reduced oxygen partial pressure with regard to the surrounding atmosphere. A further decrease of the oxidation can be achieved in that the inventive method is implemented in an inert gas atmosphere or in vacuum.

[0038] The method to produce a layer electrode can in particular be conducted with metal films of a thickness between 30 and 150 μm. Such metal films enable the production of small connection bands that exhibit a high current-carrying capacity.

[0039] Furthermore, in the inventive method a layer is preferably used that exhibits a thickness between 100 and 500 μm. Such layers are relatively thin, such that the number of the layer electrodes per volume, for example in a capacitor, can be increased, where the area available for contacting the layers increases. The ohmic resistance of the component to be produced thereby decreases in an advantageous manner.

[0040] Typically, the layer suitable for electrochemical components contains carbon. It can be implemented as carbon paper, non-woven carbon fabric, carbon fabric, or also as carbon felt.

[0041] Moreover, a plurality of fibers are also suitable for the layer that all run parallel in a preferred direction at least in sections and are connected with one another via bonding.

[0042] Such a layer has the advantage that, due to the fibers running parallel to one another in a single preferred direction, the interweave of fibers or threads (such as for example is in the case in fabrics) can be abandoned. The layer can thereby be produced cost-effectively. Moreover, since the fibers are connected with one another via bonding, the superimposition and interweaving of fibers with one another to produce the cohesion of the elements of the layer is no longer necessary, whereby it is possible to realize substantially smaller layer thicknesses for the layer, namely layer thicknesses between 10 and 500 μm.

[0043] In particular, the fibers can be activated carbon fibers that are present as lines (also known in English as “tow”).

[0044] The bonding of the fibers among one another can, for example, be generated in that a line of fibers is pierced by needles with barbs transverse to the fiber direction. After removing such needles, some fiber sections run variant to the preferred direction and are interlocked with one another. The mechanical cohesion within the layer is thereby produced. However, the proportion of the fibers comprising fiber sections variant to the preferred direction is maximally 20%, such that the fiber line clearly differentiates itself from a non-woven material where the individual fibers exhibit no preferred direction at all.

[0045] In a further exemplary embodiment of the layer, a number of fibers can be stranded with one another and thus form a thread. This exemplary embodiment of the layer has the advantage that the mechanical cohesion transverse to the preferred direction is improved in comparison to the non-stranded fibers.

[0046] Furthermore, the cited embodiment of the layer has the advantage that it enables an increased material density in comparison to fibers interwoven with one another, whereby electrochemical double-layer capacitors produced with the layer exhibit an increased capacity.

[0047] In fibers stranded with one another into a thread, the bonding of the threads, and therefore the fibers forming the threads, can also be realized among themselves via fiber sections running variant to the preferred direction that are interlocked with one another.

[0048] A further possibility to produce the mechanical cohesion of the fibers is to sew up the fibers with one another transverse to the fiber direction by means of a sewing thread. Synthetics, that are converted into carbon fibers via pyrolysis (also known as carbonization) as well as subsequent activation of the surface, are preferably used as fibers. The sewing up of the fibers with a sewing thread can either ensue before the pyrolysis and the activation of the synthetic raw material or, however, also first after the activation. As materials for the sewing thread, all materials are suitable that do not degrade the electrical properties of the electrochemical component. For the case that the electrochemical component is an electrochemical double-layer capacitor, for example polypropylene, polyethylene, or also Teflon are to be considered as sewing threads.

[0049] In order to not unnecessarily increase the layer thickness of the layer, sewing threads with a thickness between 10 μm and 50 μm are preferably used. The sewing threads can comprise an individual fiber or also a thread.

[0050] In a further embodiment of the invention, the cohesion of the fibers within the layer electrode can also be imparted in that a material acting as the bonding between the fibers is applied in places on the surface of the layer. The material imparting the bonding between the fibers can likewise be introduced in places into the layer.

[0051] All materials are suitable for this that do not degrade the electrical properties of the electrochemical component. In the case of an electrochemical double-layer capacitor, in particular materials are suitable that are inert with regard to the electrolytes uses in electrochemical double-layer capacitors. To stabilize the layer, therefore considered are, for example, carbon as a material placed or, respectively, deposited in the layer or on its surface by means of chemical vapor deposition. However, by means of chemical vapor deposition, further materials (in particular metals such as, for example, aluminum or copper) can also be brought [sic] on or in the layer.

[0052] Furthermore, the cohesion of the fibers in the layer is generated or, respectively, produced via polymer additives. Possible polymer additives are, for example, polyethylene, polypropylene, polyvinylfluoride, and tetrafluoropolyethylene. The polymer additives are preferably supplemented with a weight proportion between 2 and 20% dependent on the carbon content of the layer.

[0053] As raw material for the fibers, synthetics that comprise C₆ rings can be used with particular advantage. These synthetics can be pyrolized via heating under exclusion of air or, respectively, in an atmosphere with low oxygen content, such that they almost completely convert to carbon. This event is also known as carbonization. Subsequent to the carbonization of the fibers, the surface of the fibers can be activated via etching processes. The etching can ensue via gas treatment, for example by means of CO₂ or H₂O, as well as chemically or electrochemically. By activating the fibers, the surfaces of the fibers are greatly increased. For example, a specific surface of 3000 m²/g can be generated from a specific surface of 100 m²/g.

[0054] For example, phenol aldehyde fibers, cellulose fibers, pitch, polyvinyl alcohol and its derivatives, or also polyacrylnitrile can be used.

[0055] Furthermore, it is advantageous to use fibers with a thickness between 5 and 50 μm, since production of thin layers with a thickness between 5 and 500 μm is eased with such fibers. Given the use of very thin fibers, if necessary a plurality of fibers can also be used on top of one another in order to form the layer. Given the use of a plurality of fibers one atop the other, the layer resulting from this has the advantage of an increased mechanical stability. However, in contrast to this it is also possible that the layer comprises a single fiber layer. The thinnest layer possible given fiber strength can thereby then be produced.

[0056] Moreover, the invention specifies a layer electrode for an electrochemical component in which a surface section of a layer that lies on a metal film is pressed into a metal film. Such a layer electrode has the advantages already cited in the specification of the inventive method. In particular, it has the advantage that it can be effected thinner than conventional layer electrodes and that, due to the abandonment of the deposition of aluminum by means of an arc method, the oxidation of the aluminum, and therewith also the ohmic resistance of the layer electrode, can be reduced in an advantageous manner.

[0057] The layer applied the metal film can thereby be pressed into the metal film over its entire surface. However, it can also be that only surface sections of the layer that are separated from one another via surface sections lying free on the metal film are pressed into the metal film.

[0058] In the following, the invention is more closely explained using exemplary embodiments and the figures appertaining thereto.

[0059]FIG. 1 shows method in a schematic cross section, for example, an arrangement to implement the inventive.

[0060]FIG. 2 shows method in a schematic cross section, for example, an inventive layer electrode.

[0061]FIG. 3 shows, for example, an inventive layer electrode in plan view.

[0062]FIG. 4 shows a pressing tool lying over a stop in schematic cross section.

[0063]FIG. 5 shows a layer electrode produced with a pressing tool according to FIG. 4 in plan view.

[0064]FIG. 6 shows, for example, a further pressing tool and a stop belonging thereto.

[0065]FIG. 7 shows, for example, a layer electrode produced with pressing tool according to FIG. 6 in plan view

[0066]FIG. 8 shows, for example, a further arrangement to implement the inventive method in schematic cross section.

[0067]FIG. 1 shows an arrangement to implement the inventive method. It comprises a pressing tool 5 that is implemented in the form of a cylindrical roller. The pressing tool 5 is arranged opposite a stop 6 that is likewise implemented in the form of a cylindrical roller. The pressing tool 5 and the stop 6 rotate around the respective cylinder axis with opposite rotation direction.

[0068] Between the pressing tool 5 and the stop 6, a ribbon runs that is comprised of three partial ribbons on top of one another, forming a layer stack 4. A layer 2 or, respectively, a further layer 14 is thereby arranged on both sides of a metal film 3 (that in the example shown in FIG. 1 is an aluminum film with a thickness of 100 μm). The layers 2, 14, as well as the metal film 3, exhibit the form of ribbons that are unwound by rollers 15.

[0069] The ribbons present in the shape of a layer stack 4 are transported in a lengthwise direction (compare arrow) via the synchronously running cylindrical rollers that press against one another. At the narrowest point between the rollers, a high pressure thereby affects the layers 2, 14, such that the layers 2, 14 are pressed into the metal film 3.

[0070] However, it is necessary for this that the metal film 3 is softened. This ensues in the arrangement shown in FIG. 1, in that the pressing tool 5 and the stop 6 are heated to a temperature between 660° C. and 750° C. The heat comprised in the pressing tool 5 or, respectively, stop 6 can be conducted into the metal film 3 at the narrowest point between pressing tool 5 and stop 6 without large waste. Since the metal film 3 is an aluminum film, it has a melting point of approximately 660° C. A slight transgression of this melting temperature by both rollers that press against the aluminum film is noncritical, since an aluminum oxide present in any case on the aluminum film substantially holds the shape of the film together. The aluminum film can also, if necessary, already be preheated to approximately 600° C. at the unwinding by the roller 15, so that the film can be very quickly heated to its melting point in the pressing zone. Both rollers press with a mechanical pressure against one another, which is sufficient to press the layer 2, 14 over a portion of its thickness D into the softened aluminum film. The metal film 3 can also be thereby heated such that it liquefies in places.

[0071] In the further course of the layer stack 4, after passing both rollers pressing against one another, a layer electrode is present that presents itself as metal film 3 layered on both sides with a layer 2, 14 (compare also FIG. 2).

[0072] Furthermore, the layer 2, 14 can comprise a carbon material that is present in the form of fibers 16 interwoven with one another into a fabric. Other embodiments of the carbon material are carbon paper or, respectively, carbon non-woven material, in which the fiber direction in the order of millimeters are [sic] arranged substantially parallel to one another perpendicular to the material plane, however that exhibits no preferred direction within the material plane. The layer 2, 14 can, however, also be a line made of fibers running in parallel in a preferred direction, whereby the preferred direction coincides with the lengthwise direction of the ribbons.

[0073] The layer 2 or, respectively, 14 shown in FIG. 1 is a carbon fabric that is comprised of a plurality of fibers 16 interwoven with one another.

[0074] In order to strengthen the layers 2, 14 with metal, aluminum powder can, for example, be applied to the top of the upper layer 2 before pressing the layers 2, 14 into the metal film 3. The metal powder 11 can be applied by means of a dispersal device 12. The dispersal device 12 can, for example, be implemented according to the type of a pepper shaker.

[0075] However, the metal powder 11 can similarly be transported in the pressing zone onto the metal film 3 or even onto the pressing tool 5. The metal powder comprises particles with an average size of 5 μm to 2 mm.

[0076] Both rollers used as pressing tool 5 or, respectively, stop 6 respectively comprise an admittedly curved but smooth surface 7, 8. It can thereby be achieved that, given corresponding widths of the rollers, the layer 2 or, respectively, the layer 14 are pressed into the metal film 3 over respectively their entire surface. An optimal electrical contact is thereby achieved between the metal film 3 and the layer 2 or, respectively, 14.

[0077] The metal film 3 coated with the layers 2, 14 can be separated transverse to the lengthwise direction of the ribbon into individual sections that subsequently, stacked on top of one another, result in capacitor winding of a capacitor. The layers 2, 14 can exhibit a width of, for example, approximately 15 cm, while the metal film 3 exhibits a width of, for example, approximately 22 cm. An excess length thereby ensues for the metal film 3 that can be guided in the form of a small connection band to an external connection of the capacitor.

[0078] In addition to the heating of the pressing tool 5 or, respectively, of the stop 6, the softening or, respectively, melting of the metal film 3 can also be caused via an electrical current. The electrical current can either flow between pressing tool 5 and stop 6 or, however, also between metal film 3 and pressing tool 5 or between metal film 3 and stop 6. It is thereby substantially irrelevant whether the electric current flows to the left between the uncoated metal film 3 from both rollers or whether the electric current flows to the right through the coated metal film 3 from both rollers. In all cases, the highest electrical resistance of the current path at the contact point lies either between pressing tool 5 and stop 6 or between aluminum film 3 and pressing tool 5 or, respectively, stop 6, such that heat caused by the current is substantially generated there. Via the control of the current or, respectively, the applied voltage, the heat generated in the heating zone between pressing tool 5 and stop 6 can be precisely controlled.

[0079] A further possibility to soften or, respectively, melt the metal film 3 is to use ultrasound rollers as pressing tool 5 or, respectively, stop 6. Very generally, in another manner ultrasonic power is radiated into the pressing zone between pressing tool 5 and stop 6, whereby the metal film 3 softens or, respectively, melts.

[0080] The cited methods to soften the metal film 3 can be used in all possible embodiments of pressing tool 5 and stop 6.

[0081]FIG. 2 shows a metal film 3 layered with a layer 2 or, respectively, 14, as it results from a method implemented according to FIG. 1. One recognizes that the fibers 16 of the layers 2, 14 are not pressed into the metal film 3 over their entire thickness d. They are merely embedded over a portion of their thickness d into the metal film 3. It is thereby ensured that a sufficient surface of the layer 2, 14 remains that must interact with an electrolyte, for example in an electrochemical double-layer capacitor, to form its capacity. Such an interaction would not be possible when the layer 2, 14 or, respectively, their fibers 16 were pressed into the metal film 3 over the entire thickness.

[0082] One recognizes in addition that a large-surface direct contact is produced within the metal film 3 to the material of the layer 2 or, respectively, 14, thus for example the fiber 16.

[0083]FIG. 3 shows in plan view a metal film 3 coated with a layer 2 as it results from the method shown in FIG. 1. The metal film 3 has a somewhat larger width as the layer 2, whereby an excess length is realized that can be used as small connection bands for contacting the metal film 3 with an external connection of an electrical component. Furthermore, it arises from FIG. 3 that the layer 2 is pressed into the metal film 3 over its entire surface, which means as much as that the surface section 1 corresponds to the entire surface of the layer 2.

[0084]FIG. 4 shows in cross section a pressing tool 5 and a stop 6 as it can be used in an arrangement according to FIG. 1. In contrast to the portrayal in FIG. 1, the surface 7 of the pressing tool 5 and the surface 8 of the stop 6 is [sic] not smooth, but rather is provided with elevations 9 or, respectively, depressions 18. These elevations 9 have the shape of annular protrusions rotating in the circumferential direction around the cylindrical rollers. The elevations 9 and the arrangement of pressing tool 5 and stop 6 are thereby selected such that a elevation 9 of the pressing tool 5 impacts a elevation 9 of the stop 6. The elevations 9 of the pressing tool 5 this lie congruent over the elevations 9 of the stop 6. The same is true for the depressions 18. Via a use of pressing tool 5 or, respectively, stop 6 according to FIG. 4, it can be achieved that the surface sections 1 of the layers 2, 14 (that are pressed into the metal film 3) are separated from one another by surface sections 10 of the layers 2, 14 that lie free on the metal film 3.

[0085] This is shown in FIG. 5. FIG. 5 shows in plan view a coated metal film 3 produced with an arrangement according to FIG. 1 using pressing tool 5 and stop 6 according to FIG. 4. The depiction according to FIG. 5 corresponds to the dimensions of the depictions in FIG. 3. In contrast to FIG. 3, the surface sections 1 (in which the layer 2 is pressed into the metal film 3) now run along lengthwise paths and are separated from one another by further lengthwise paths that represent sections 10 of the layer 2 that lie free on the metal film 3. Via such an arrangement, it can be achieved that the surface of the layer 2 active for the function in the electrochemical component is further enlarged, since the layer 2 is partially not embedded in the metal film 3 at all.

[0086]FIG. 6 shows a further embodiment of pressing tool 5 or, respectively, stop 6 as it can be used in an arrangement to implement the inventive method according to FIG. 8. The surface 7, 8 of the pressing tool 5 or, respectively, of the stop 6 respectively facing the layer 2 or, respectively, 14 is thereby shown. The pressing tool 5 is characterized by a flat surface 7, that comprises elevations in the shape of small cubes. The counterpart to pressing tool 5, namely the stop 6, comprises on the other hand a flat, even surface 8. Given layer stack lying between the pressing tool 5 and the stop 6 according to FIG. 8 and pressing of the pressing tool 5 against the stop 6, a layered metal film 3 according to FIG. 7 results, where the layered metal film 3 is shown in plan view.

[0087] The arrangement of the protrusion 9 of the pressing tool 5 are [sic] designed such that all fibers 16 are contacted with the metal film 3. In particular for the one-dimensionally structured fiber lines, it is important to allow no non-contacted fibers 16 along the lengthwise direction of the electrode.

[0088]FIG. 7 shows a coated metal film 3 with dimensions that correspond to the depictions in FIG. 5 or, respectively, FIG. 3. In the implementation of the method according to FIG. 8, the layer 2 is connected with the metal film 3 in lengthwise sections 13. However, the pressing of the layer 2 into the metal film 3 ensues only at such locations at which the elevations 9 of the pressing tool 5 are located. At these locations are located surface sections 1 at which the layer 2 is pressed into the metal film 3. At all remaining surfaces, sections 10 of the layer 2 ensue that lie free on the metal film 3. The metal film 3 shown in FIG. 7 has the same advantages as the metal film 3 shown in FIG. 5, however the surface portion of the pressed-in section of the layer 2 is still further reduced, whereby the active material portion of the layer 2 available for the function of the component, for example for a capacitor, is still further increased. For example, via a coated metal film 3 according to FIG. 7, an electrochemical double capacitor can be realized with increased capacity with regard to a capacitor with a coated metal film 3 according to FIG. 5.

[0089]FIG. 8 shows a further arrangement to implement the inventive method that is similar to that shown in FIG. 1. In contrast to FIG. 1, a stamp that can be moved transverse to the ribbon direction and is otherwise stationary is used as a pressing tool 5, and a stationary block is used as a stop 6. Since in this arrangement pressing tool 5 and stop 6 can no longer transport a layer stack 4 made of a plurality of ribbons in the lengthwise direction, it is necessary to provide an additional ribbon transport device.

[0090] The method to produce a layer electrode according to FIG. 8 is implemented in that the ribbon transport device 17 transports the ribbons of layer 2, metal film 3, and layer 14 lying on top of one another over a lengthwise section 13. The pressing tool 5 is subsequently pressed on the stop 6, whereby depending on implementation of the surface 7 of the pressing tool 5 a more or less large surface section 1 of the layers 2, 14 is pressed into the metal film 3. The pressing tool 5 subsequently goes up, whereby the layer stack 4 is released for a further transport step over a lengthwise section 13 by means of the ribbon transport device 17. Through this, a discontinuous method is made available in that successive lengthwise sections 13 of the layers 2, 14 are pressed into the metal film 3. The ribbon transport device 17 can, for example, be realized by means of rollers pressed on the layer stack, as they were also already shown according to FIG. 1. In contrast to FIG. 1, the rollers must not necessarily be electrically conductive, as would be necessary to heat the metal film 3 by means of an electrical current.

[0091] In the coated metal films according to the FIGS. 3, 5, and 7, an uncoated edge of the metal film 5 remains that is not coated and that, in the further course of the production, serves for contacting the metal film 3 to external connections of the capacitor.

[0092] In addition to the aluminum films cited in FIG. 1, other metal films, for example copper films, can also be used.

[0093] In addition to the layers specified in FIG. 1 comprised of fibers lying in parallel, carbon paper, carbon non-woven material, or carbon felt are also considered as carbon fabric. In contrast to the fibers running in parallel in a preferred direction in a line, given the paper and given the non-woven material it is a two-dimensional formation, while given felt carbon fibers run in three dimensions, this in all three spatial directions.

[0094] The specified invention is not limited to electrochemical double-layer capacitors, but rather can likewise be used for other electrochemical components such as batteries or asymmetrical capacitors in which the charge storage is realized by the pseudocapacity of one or both electrode layers. It is accordingly also not necessary that the used layers 2 or, respectively, 14 comprise activated carbon fiber material. The activation of the carbon material is merely advantageous for the use of the layer electrodes in electrochemical double-layer capacitors.

[0095] The invention is not limited to the presented exemplary embodiments, but rather is defined in its most general form by patent claim 1. 

1. Method to produce a layer electrode for electrochemical components with a layer (2, 14) applied to a metal film (3), whereby to produce a connection between the metal film (3) and the layer (2, 14) a surface section (1) of the layer (2, 14) is pressed into the metal film (3) over a portion of the thickness of the layer (2, 14), and whereby the metal film (3) is softened during the pressing, whereby the layers (2, 4) [sic] as well as the metal film (3) are respectively ribbon-shaped and are respectively fed to the pressing tool by a roller (15).
 2. Method according to claim 1, whereby a layer (2, 14) comprising elementary carbon is used.
 3. Method according to any of the claims 1 or 2, whereby an aluminum film is used as a metal film (3).
 4. Method according to any of the claims 1 through 3, whereby a layer stack (4) with a layer (2, 14) lying over a metal film (3) is placed between a pressing tool (5) and a stop (6), and whereby the pressing tool (5) is pressed against the stop (6).
 5. Method according to claim 4, whereby a flat surface (7) of the pressing tool (5) is pressed against a flat surface (8) of the stop (6).
 6. Method according to claim 4, whereby a surface of the pressing tool (5) comprising depressions (18) is pressed against a stop (6) whose surface is fashioned such that, at the locations of the depressions (18), the layer (2, 14) is not pressed into the metal film (3).
 7. Method according to any of the claims 1 through 6, Whereby the metal film (3) is softened in the proximity of the pressing tool (5).
 8. Method according to any of the claims 1 through 7, whereby the metal film (3) is softened by heating by means of a heated pressing tool (5) or a heated stop (6).
 9. Method according to any of the claims 1 through 7, whereby the metal film (3) is softened via an electrical current flowing through the metal film (3).
 10. Method according to any of the claims 1 through 7, whereby the metal film (3) is softened via emission of ultrasound.
 11. Method according to any of the claims 1 through 10, whereby before the production of the connection between the layer (2) and the metal film (3), metal powder (11) is applied to the surface section (1) to be pressed.
 12. Method according to any of the claims 1 through 11, whereby respectively a layer (2, 14) is connected with the metal film (3) on top of and on the underside of the metal film (3), whereby the layers (2, 14) are congruent to one another.
 13. Method according to any of the claims 4 through 12, whereby a cylindrical roller rotating around the cylinder axis is used as a pressing tool (5) that rolls on the layer stack (4).
 14. Method according to any of the claims 1 through 12, whereby the layer stack (4) comprises the shape of a ribbon, and whereby a stamp that can be moved transverse to the layer is used as a pressing tool (5), with the following steps: a) press the stamp and an intermediate lengthwise section (13) of the ribbon against a stop (6) b) move the stamp transverse to the ribbon to release the ribbon c) move the ribbon in the lengthwise direction by means of a ribbon transport device (17).
 15. Method according to any of the claims 1 through 14, whereby the production of the connection between the layer (2, 14) and the metal film (3) ensues in a reduced oxygen partial pressure with regard to the surrounding atmosphere.
 16. Method according to any of the claims 1 through 14, whereby the production of the connection between the layer (2, 14) and the metal film (3) ensues in an inert gas atmosphere.
 17. Method according to any of the claims 1 through 16, whereby a metal film (3) with a thickness between 30 and 150 μm is used.
 18. Method according to any of the claims 1 through 17, whereby a layer (2, 14) with a thickness of 100 to 500 μm is used.
 19. Method according to any of the claims 1 through 18, whereby a carbon paper, carbon non-woven material, or carbon felt is used as a layer (2, 14).
 20. Method according to any of the claims 1 through 18, whereby a layer (2, 14) is used that is comprised of a plurality of fibers (16) running at least in sections in parallel in a preferred direction, and in that the fibers (16) are connected with one another via bonding.
 21. Layer electrode for electrochemical components, in that a surface section (1) of a layer (2, 14) applied to a metal film (3) is pressed into the metal film (3).
 22. Layer electrode according to claim 21, in that the layer (2, 14) is pressed over its entire surface into the metal film (3).
 23. Layer electrode according to claim 21, in that the surface sections (1) of the layer (2, 14) pressed into the metal film (3) are separated from one another by surface sections (10) lying free on the metal film (3). 